| COMPOSICIÓN QUÍMICA |
% |
| Al₂O₃ (peso %) |
≥ 70 |
80,0 |
92,5 |
92,0 ± 0,5 |
≥ 92,8 |
| ZrO₂ |
≥ 17 |
10,0 |
≥ 5,0 |
/ |
/ |
| SiO₂ |
/ |
5,0 |
/ |
4,5 |
≤ 5 |
| Others |
< 13,0 |
< 5,0 |
< 2,2 |
< 3,0 |
< 2,2 |
| CARACTERÍSTICAS FÍSICAS |
|
| Specific weight(g/cm³) |
4,5 ± 0,05 |
3,7 |
≥3,7 |
3,70 ± 0,03 |
≥ 3,70 |
| Bulk density (g/cm³) |
2,3 |
2,2 |
2,2 |
2,2 |
2,2 |
| Mohs hardness |
8 |
9 |
9 |
9 |
9 |
| Vickers hardness (HV) |
1100 |
1000 |
1150 |
1600 |
1470 |
| Water absorption (%) |
≤ 0,01 |
≤ 0,01 |
≤ 0,01 |
≤ 0,01 |
≤ 0,01 |
| DIÁMETROS Y TIPOS |
|
| Diámetros disponibles |
From 3 to 20 mm |
From 3 to 20 mm |
From 3 to 20 mm |
From 3 to 20 mm |
From 3 to 20 mm |
| Tipos |
ZTA MICREOBEADS |
ZTA MICREOBEADS |
ALUMINA MICROBEADS |
ALUMINA MICROBEADS |
ALUMINA MICROBEADS |